Acrylic Polyurethane Coating

• Customization: Available
• Main Raw Material: Polyurethane
• Appearance: Solvent
• Model NO.: J4415
• State in Container: Uniform, Easy to Stir
• Viscosity (Coating-4), S: ≥60
• Fineness, μm: ≤35
• Non-Volatile Content, %: ≥60
• Applicability: No Abnormalities
• Surface Drying Time, H: 1
• Full Drying Time, H: 24
• Baking Time, M: 60 (80ºC)
• Coating Color and Appearance: Meets Standard Sample, Coating Smooth, Uniform Col
• Scratch Test: Grade 2 Pass
• Transport Package: Drum
• Specification: 15kg/piece
• Trademark: JIREN
• Origin: China
• Production Capacity: 50000ton/Year

Product Description

Design Purpose: Primarily suitable for decorative coatings of indoor steel components, steel products, and instruments.

Product Characteristics: Uniform and aesthetically pleasing colors, comfortable feel, strong adhesion, water and oil resistance, excellent physical and chemical properties.

Product Composition: Acrylic resin, polyurethane, pigments, organic solvents, and additives.

Product Appearance: Various conventional colors, but white is not suitable.

Technical Specifications: The product should meet the following technical requirements:
 

Item

Specification

Test Methods

1. State in container

Uniform, easy to stir

GB3186-82 (89)

2. Viscosity (coating-4), S

≥60

GB/T1723-93

3. Fineness, μm

≤35

GB6753.1-86

4. Non-volatile content, %

≥60

GB/T6751

5. Applicability

No abnormalities

GB1757-79 (89)

6. Surface drying time, h

1

GB/T1728 Method B

7. Full drying time, h

24

GB/T1728 Method B

8. Baking time, m

60 (80ºC)

GB9273-88

9. Coating color and appearance

Meets standard sample, coating smooth, uniform color

GB9761-88

10. Scratch test

Grade 2 pass

GB/T9286-1998

11.Pencil hardness

HB grade pass

GB/T6739-1996

12.Water resistance

No significant changes after 240h immersion

GB/T1733-93 Method A

13.Oil resistance

No significant changes after 240h immersion

GB9274-88 Method A

 
Packaging Specification: 15kg/3kg
 

Construction Conditions:

Surface treatment:

1.Steel should be sandblasted to Sa2.5 or manually derusted to St3, with surface roughness of 40-70μm, ensuring the substrate surface is clean and dry.
2.After meeting the rust removal standards, primer application should be completed within 4 hours. Surfaces not coated in time should be reprocessed.
3.Prior to applying the topcoat, ensure the primer surface is clean and dry.

Temperature and Humidity:

1.Substrate temperature should be 0 to 50°C, and at least 3°C above the dew point. Relative humidity should not exceed 85%.

 

Construction parameter:
Mixing Ratio: As provided by supplier

Application Method: Spraying

Usability Period: 4 hours (23°C)

Thinner: Polyurethane thinner

Shelf Life: 1 year from the date of manufacture under normal storage and transportation conditions.
 

Safety Precautions:

1. Ensure adequate ventilation at the work site.
2. No smoking or open flames in the work area and nearby zones.
3. Use explosion-proof electrical equipment.
4. No metal impacts allowed.
5. Prevent static electricity accumulation.
6. Wear necessary protective gear.
7. Avoid inhalation of paint mist and contact with paint and thinner.
8. In case of eye contact with paint, rinse with plenty of water and seek medical attention promptly.
9. Properly dispose of empty paint cans and leftover paint to avoid environmental pollution.
10. Take all other necessary safety and fire prevention measures based on the specific site conditions.